Polyurethane round bars
| UN. | NORME STANDARDS |
60 | 80 | 85 | 90 | 95 | |
| CARATTERISTICHE ORIGINALI ORIGINAL FEATURES |
|||||||
| DUREZZA SH A HARDNESS |
Sh A | DIN 53505 | 60 | 79 | 85 | 88 | 96 |
| DENSITA’ DENSITY |
gr/cm3 | DIN 53479 | 1,07 | 1,10 | 1,11 | 1,13 | 1,15 |
| ALLUNGAMENTO A ROTTURA ULTIMATE ELONGATION |
% | DIN 53504 | 340 | 680 | 570 | 450 | 410 |
| CARICO DI ROTTURA ULTIMATE TENSILE STRENGHT |
kg/cm2 | DIN 53504 | 205 | 225 | 300 | 330 | 350 |
| RESISTENZA ALLA LACERAZIONE TEAR RESISTANCE |
kg/cm | ASTM D 624 C | 19 | 47 | 71 | 74 | 85 |
| ABRASIONE ABRASION |
mm3 | DIN 53516 | 42 | 38 | 38 | 36 | 36 |
| RESILIENZA RESILIENCE |
% | DIN 53512 | 56 | 50 | 50 | 45 | 41 |
| DEFORMAZIONE PERMANENTE (70 h a temperatura ambiente) PERMANENT DEFORMATION (70 h at room temperature) |
% | DIN 53517 | 16 | 15 | 14 | 14 | 16 |
| (METODO B dopo 22 h a 70°C) (METHOD B after 22 h at 70°C) |
% | DIN 53517 | 30 | 30 | 30 | 30 | 31 |
| INVECCHIAMENTO IN ARIA (70 h a 100°C) AGEING IN AIR (70 h at 100°C) |
ASTM D 513 | ||||||
| VARIAZIONE DUREZZA HARDNESS VARIATION |
sh A | 0 | 0 | 0 | 0 | 0 | |
| VARIAZIONE ALLUNGAMENTO ELONGATION VARIATION |
% | -10 | -9 | -6 | -6 | -9 | |
| VARIAZIONE CARICO DI ROTTURA TENSILE STRENGHT VARIATION |
% | -10 | -10 | -7 | -7 | +5 | |
| INVECCHIAMENTO IN OLIO ASTM N.3 (70 h a 100°C) SUBMERSION IN OIL ASTM No.3 (70 h a 100°C) |
ASTM D 471 | ||||||
| VARIAZIONE DUREZZA HARDNESS VARIATION |
sh A | 0 | 0 | 0 | 0 | 0 | |
| VARIAZIONE ALLUNGAMENTO ELONGATION VARIATION |
% | -10 | -5 | -5 | -11 | -11 | |
| VARIAZIONE CARICO DI ROTTURA TENSILE STRENGHT VARIATION |
% | -10 | -8 | 0 | -11 | -11 | |
| VARIAZIONE IN VOLUME VOLUME VARIATION |
% | +21 | +18 | +16 | +15 | +14 | |
| INVECCHIAMENTO IN OLIO ASTM N.5 (70 h a 100°C) SUBMERSION IN OIL ASTM No.5 (70 h a 100°C) |
ASTM D 471 | ||||||
| VARIAZIONE DUREZZA HARDNESS VARIATION |
sh A | 0 | 0 | 0 | 0 | 0 | |
| VARIAZIONE ALLUNGAMENTO ELONGATION VARIATION |
% | -10 | -9 | -7 | -9 | -10 | |
| VARIAZIONE CARICO DI ROTTURA TENSILE STRENGHT VARIATION |
% | -11 | -9 | -7 | -6 | -10 | |
| VARIAZIONE IN VOLUME VOLUME VARIATION |
% | +11 | +9 | +6 | +5 | +4 | |
| RESISTENZA ALLE BASSE TEMPERATURE LOW TEMPERATURE RESISTANCE |
ASTM D 1329 | ||||||
| TR 10 | °C | -35 | -34 | -33 | -32 | -32 | |
| TR 30 | °C | -31 | -30 | -28 | -21 | -21 | |
| TR 50 | °C | -23 | -21 | -20 | -12 | -12 | |
| TR 70 | °C | -15 | -15 | -12 | -6 | -6 | |
| TEMPERATURA DI INFRAGILIMENTO BRITTLE TEMPERATURE |
°C | ASTM D 746 | -57 | -56 | -55 | -55 | -55 |